物理特性(Physical Properties) | ||||||||
纤维(Fiber): | 100%PTFE聚四氟乙烯 | |||||||
基布(Scrim): | 100%PTFE聚四氟乙烯 | |||||||
重量(Weight/Tolerance):(g/m2) | 780±10% | |||||||
厚度(Thickness/Tolerance):(mm) | 1.2±0.2 | |||||||
化学处理(Chemical Finish): | 热定型,覆PTFE微孔膜 | |||||||
透气性(Air Permeability/Tolerance):(l/dm2/min@200pa) | 20-40 | |||||||
断裂强度(Typical Load @ Peak) (N/5cm) | 经向(MD): | 700 | 纬向(XD): | 700 | ||||
断裂伸长率(Typical Strain @ Peak) | 经向(MD): | 10% | 纬向(XD): | 25% | ||||
伸长率 @50N (Typical Strain @ 50N) | 经向(MD): | 1.5% | 纬向(XD): | 3% | ||||
化学特性(Chemical Properties) | ||||||||
抗酸性(Acids Resistance): | 优 | |||||||
抗碱性(Alkalis Resistance): | 优 | |||||||
抗水解性(Hydrolysis Resistance): | 优 | |||||||
抗氧化性(Oxidize Resistance): | 优 | |||||||
抗磨损性(Abrasion Resistance): | 优 | |||||||
温度特性(Temperature) | ||||||||
连续运行温度(Maximum Operation Temperature): | (℃) | 250(Dry) | ||||||
瞬间运行温度(Maximum Surge Temperature): | (℃) | 260(Dry) |
物理特性(Physical Properties) | ||||||||
纤维(Fiber): | 100%PTFE聚四氟乙烯 | |||||||
基布(Scrim): | 100%PTFE聚四氟乙烯 | |||||||
重量(Weight/Tolerance):(g/m2) | 780±10% | |||||||
厚度(Thickness/Tolerance):(mm) | 1.2±0.2 | |||||||
化学处理(Chemical Finish): | 热定型,覆PTFE微孔膜 | |||||||
透气性(Air Permeability/Tolerance):(l/dm2/min@200pa) | 20-40 | |||||||
断裂强度(Typical Load @ Peak) (N/5cm) | 经向(MD): | 700 | 纬向(XD): | 700 | ||||
断裂伸长率(Typical Strain @ Peak) | 经向(MD): | 10% | 纬向(XD): | 25% | ||||
伸长率 @50N (Typical Strain @ 50N) | 经向(MD): | 1.5% | 纬向(XD): | 3% | ||||
化学特性(Chemical Properties) | ||||||||
抗酸性(Acids Resistance): | 优 | |||||||
抗碱性(Alkalis Resistance): | 优 | |||||||
抗水解性(Hydrolysis Resistance): | 优 | |||||||
抗氧化性(Oxidize Resistance): | 优 | |||||||
抗磨损性(Abrasion Resistance): | 优 | |||||||
温度特性(Temperature) | ||||||||
连续运行温度(Maximum Operation Temperature): | (℃) | 250(Dry) | ||||||
瞬间运行温度(Maximum Surge Temperature): | (℃) | 260(Dry) |